Magnet SmCo
| SmCo tersinterMagnetCiri-ciri fizikal | |||||||||
| bahan | Gred | Remanence | Rev. Temp.- Coeff. Daripada Br | Paksaan Paksa | Daya Paksaan Intrinsik | Rev. Temp.-Coeff. Daripada Hcj | Maks. Produk Tenaga | Maks. Suhu Operasi | Ketumpatan |
| Br (KGs) | Hcb (ANDA) | Hcj (ANDA) | (BH) maks. (MGOe) | g/cm³ | |||||
| SmCo5 | XG16 | 8.1-8.5 | -0.050 | 7.8-8.3 | 15-23 | -0.30 | 14-16 | 250 ℃ | 8.3 |
| XG18 | 8.5-9.0 | -0.050 | 8.3-8.8 | 15-23 | -0.30 | 16-18 | 250 ℃ | 8.3 | |
| XG20 | 9.0-9.4 | -0.050 | 8.5-9.1 | 15-23 | -0.30 | 19-21 | 250 ℃ | 8.3 | |
| XG22 | 9.2-9.6 | -0.050 | 8.9-9.4 | 15-23 | -0.30 | 20-22 | 250 ℃ | 8.3 | |
| XG24 | 9.6-10.0 | -0.050 | 9.2-9.7 | 15-23 | -0.30 | 22-24 | 250 ℃ | 8.3 | |
| XG16S | 7.9-8.4 | -0.050 | 7.7-8.3 | ≥23 | -0.28 | 15-17 | 250 ℃ | 8.3 | |
| XG18S | 8.4-8.9 | -0.050 | 8.1-8.7 | ≥23 | -0.28 | 17-19 | 250 ℃ | 8.3 | |
| XG20S | 8.9-9.3 | -0.050 | 8.6-9.2 | ≥23 | -0.28 | 19-21 | 250 ℃ | 8.3 | |
| XG22S | 9.2-9.6 | -0.050 | 8.9-9.5 | ≥23 | -0.28 | 21-23 | 250 ℃ | 8.3 | |
| XG24S | 9.6-10.0 | -0.050 | 9.3-9.9 | ≥23 | -0.28 | 23-25 | 250 ℃ | 8.3 | |
| Sm2Co17 | XG24H | 9.5-10.2 | -0.025 | 8.7-9.6 | ≥25 | -0.20 | 22-24 | 350 ℃ | 8.3 |
| XG26H | 10.2-10.5 | -0.030 | 9.4-10.0 | ≥25 | -0.20 | 24-26 | 350 ℃ | 8.3 | |
| XG28H | 10.3-10.8 | -0.035 | 9.5-10.2 | ≥25 | -0.20 | 26-28 | 350 ℃ | 8.3 | |
| XG30H | 10.8-11.0 | -0.035 | 9.9-10.5 | ≥25 | -0.20 | 28-30 | 350 ℃ | 8.3 | |
| XG32H | 11.0-11.3 | -0.035 | 10.2-10.8 | ≥25 | -0.20 | 29-32 | 350 ℃ | 8.3 | |
| XG22 | 9.3-9.7 | -0.020 | 8.5-9.3 | ≥18 | -0.20 | 20-23 | 300 ℃ | 8.3 | |
| XG24 | 9.5-10.2 | -0.025 | 8.7-9.6 | ≥18 | -0.20 | 22-24 | 300 ℃ | 8.3 | |
| XG26 | 10.2-10.5 | -0.030 | 9.4-10.0 | ≥18 | -0.20 | 24-26 | 300 ℃ | 8.3 | |
| XG28 | 10.3-10.8 | -0.035 | 9.5-10.2 | ≥18 | -0.20 | 26-28 | 300 ℃ | 8.3 | |
| XG30 | 10.8-11.0 | -0.035 | 9.9-10.5 | ≥18 | -0.20 | 28-30 | 300 ℃ | 8.3 | |
| XG32 | 11.0-11.3 | -0.035 | 10.2-10.8 | ≥18 | -0.20 | 29-32 | 300 ℃ | 8.3 | |
| XG26M | 10.2-10.5 | -0.035 | 8.5-9.8 | 12-18 | -0.20 | 24-26 | 300 ℃ | 8.3 | |
| XG28M | 10.3-10.8 | -0.035 | 8.5-10.0 | 12-18 | -0.20 | 26-28 | 300 ℃ | 8.3 | |
| XG30M | 10.8-11.0 | -0.035 | 8.5-10.5 | 12-18 | -0.20 | 28-30 | 300 ℃ | 8.3 | |
| XG32M | 11.0-11.3 | -0.035 | 8.5-10.7 | 12-18 | -0.20 | 29-32 | 300 ℃ | 8.3 | |
| XG24L | 9.5-10.2 | -0.025 | 6.8-9.0 | 8-12 | -0.20 | 22-24 | 250 ℃ | 8.3 | |
| XG26L | 10.2-10.5 | -0.035 | 6.8-9.4 | 8-12 | -0.20 | 24-26 | 250 ℃ | 8.3 | |
| XG28L | 10.3-10.8 | -0.035 | 6.8-9.6 | 8-12 | -0.20 | 26-28 | 250 ℃ | 8.3 | |
| XG30L | 10.8-11.5 | -0.035 | 6.8-10.0 | 8-12 | -0.20 | 28-30 | 250 ℃ | 8.3 | |
| XG32L | 11.0-11.5 | -0.035 | 6.8-10.2 | 8-12 | -0.20 | 29-32 | 250 ℃ | 8.3 | |
| Catatan: · Kami tetap sama seperti di atas melainkan dinyatakan daripada pelanggan. Suhu kari dan pekali suhu adalah untuk rujukan sahaja, bukan sebagai asas untuk membuat keputusan.· Suhu kerja maksimum magnet boleh berubah disebabkan nisbah panjang dan diameter dan faktor persekitaran. | |||||||||
Kelebihan:
Penggunaan magnet ini dikondisikan oleh suhu dalam julat luas dari 250ºC hingga 350ºC dan suhu Curie mereka boleh setinggi
sebagai 710 hingga 880 °C. Oleh itu, magnet SmCo mempunyai kestabilan magnet yang terbaik kerana rintangan unggul terhadap suhu tinggi.
Magnet SmCo dicirikan oleh rintangan kakisan yang sangat tinggi, tiada salutan diperlukan untuk perlindungan permukaan.
ciri:
Kelemahan magnet SmCo ialah kerapuhan bahan yang ketara – faktor yang mesti diambil kira terutamanya semasa pemprosesan.
Magnet tergalvani atau disalut oleh elektrodeposisi katodik untuk aplikasi tertentu.
Permohonan:
Di kawasan suhu operasi yang tinggi, rintangan kakisan dan pengoksidaan yang tinggi adalah penting. Seperti, Magnetron elektronik,Magnetpenghantaran ic,
Rawatan magnet, Magnistor, dsb.
Semua nilai yang dinyatakan telah ditentukan menggunakan sampel standard mengikut IEC 60404-5. Spesifikasi berikut berfungsi sebagai nilai rujukan dan mungkin
berbeza. Maks. suhu operasi bergantung kepada dimensi magnet dan aplikasi khusus. Untuk maklumat lanjut sila hubungi kami
jurutera aplikasi.